Shanghai Kai Fu Industrial Co., Ltd. focus on wholesale sales of M35 high speed steel for more than ten years, as has been the quality, price, service attitude of the three recognized by our customers! The wholesale and retail of M35 high speed steel contact, the national toll free hotline: 400-632-0358. phone: 021-67893937 Fax: 021-67762056., mobile phone number: 18821119505 official QQ:2863585986.
Characteristics of application of M35 cobalt high speed steel compared to low price and easy processing, by proper heat treatment, can obtain high hardness (HRC67 ~ 70), high red hardness (625 DEG C for 4 hours, HRC63 to 65) and high wear resistance, toughness and flexural strength are not less than the ordinary high speed steel, can overcome the mold edge collapse and crack of the early damage
特性应用M35含钴高速钢相比价格低廉且易加工,通过适当的热处理,可得到高硬度(HRC67～70),高红硬性(625℃4小时,HRC63～65)和高耐磨性,韧性和抗弯强度均不低于普通型高速钢,可克服模具刃口塌陷和崩裂等早期损坏.
M35高速钢主要特性是含Co通用切削工具模具钢，淬硬度是1200—1240C。标准比较：AISI－M2JIS－SKH51。出厂状态：球化退火<225。特性与应用：此钢为钨钢高速。宜于制造强力切割用耐磨、耐冲击各种工具，高级冲模，螺丝模，较需韧性及形状复杂工具，铰刀、铣刀、铁头、冲头等。锻造温度：1100－900℃
The main characteristics of M35 high speed steel containing Co general cutting tool die steel, quenching hardness is 1200 – 1240C. Standard: AISIM2JISSKH51. Factory state: spheroidizing annealing <225. Features: the steel tungsten steel high speed. Suitable for manufacturing of powerful cutting and abrasion resistance, impact of various tools, advanced die, die, than the required toughness and complex shaped tool, milling cutter, reamer, iron head, punch etc.. Forging temperature: 1100900 C
The annealing temperature: heating to 800 – 850 ℃, the temperature for 2 to 4 hours, the cooling in the furnace. The cooling medium: air cooling, oil, grading (550 – 580 ℃) typical chemical composition (mass fraction,%): C0.88 ~ 0.95, Mn ≤ 0.40, Si ≤ 0.40, Cr3.80 ~ 4.50, Mo4.75 ~ 5.20, V1.75 ~ 2, W6.00 ~ 7, P ≤ 0.030, S ≤ 0.030, Co4.60 ～ 5.
Refer to the corresponding grades: standard of our country GB steel W6Mo5Cr4V2Co5, AISI standard M35 America steel, the Japanese JIS standard grades SKH55/SKH58, Japan YXM4, Japan HITACHI standard steel Hitachi Datong DAIDO standard grades MH55, Nachi NACHI standard grades HM35, German DIN Standard Steel No. 1.3243, Austria Bai Lu BOHLER standard grades S705, France NF standard grades Z100DCWV (09-04-02-02).
退火温度：加热至800－850℃，在此温度停留2－4小时，在炉中任其渐冷。冷却介质：空冷，油，分级（550－580℃）典型化学成分（质量分数，%）：C0.88～0.95、Mn≤0.40、Si≤0.40、Cr3.80～4.50、Mo4.75～5.20、V1.75～2.00、W6.00～7.00、P≤0.030、S≤0.030、Co4.60～5.00。
参考对应钢号：我国GB标准钢号W6Mo5Cr4V2Co5、美国AISI标准钢号M35、日本JIS标准钢号SKH55/SKH58、日本日立HITACHI标准钢号YXM4、日本大同DAIDO标准钢号MH55、日本不二越NACHI标准钢号HM35、德国DIN标准钢号1.3243、奥地利百禄BOHLER标准钢号S705、法国NF标准钢号Z100DCWV（09-04-02-02）。